ENAMELS



SR 235

The red enamel SR 235 is made with epoxy esters and high chemical resistance pigments. It is suitable when a finish with special chemical agents and friction protections, combined to a strong adhesivity to supports to paint is required. It is compatible with all types of enamelled wire. It features high dielectric resistance and a very good water and saline resistance. It can be also supplied in the colours green and black.

Characterists

VALUE
Colour Bright red RAL 3002
Density 25°C 1,150 - 1,250
Viscosity 25°C 900 - 1200 mPa.s
Dry residual 135°C 59% - 61%
Drying up time on copper at 25°C 160' - 180'
Corrosion on copper Absent
Dielectric strength >6000 v/0,1 mm


SR 260

The enamel SR 260 is made with modified epoxy resins specifically designed for anti-trace coverings. It forms a film with special characteristics of hardness and of chemical agents and superficial discharge resistance, with values comparable to those ones of ceramics materials. It is recommended for security and high quality coverings.

Characterists

VALUE
Colour (A) red - (B) white
Density 25°C (dopo miscelaz.) (A) 1,10-1,20 gr/ml - (B) 1,10-1,20 gr/ml
Dielectric strength 3000-5000 V/0,1mm


SR 269

The red enamel SR 269 is made with special resins desgned to obtain very good oil and chemical agents resistance. It is suitable for finishes on coil band, on stators, for finish of cowls in mica and for protecting all type of electrical equipments. It has a rapid essication and it is compatible with all types of enamelled wire. It can be also supplied in the colour black and in tropicalized version.

Characterists

VALUE
Colour Bright red RAL 3002
Density 25°C 1,180 - 1,19 gr/ml
Viscosity 25°C 550 - 570 mPa.s
Dry residual 135°C 57% - 59%
Drying to the touch at 25°C 60' - 80'
Corrosion on copper Absent
Dielectric strength >4900 V/0,1mm